| RP SERIES, RUBBER AND PLASTIC BONDING CYANOACRYLATES |
| PRODUCT | BASE | COLOR | GAP FILL | VISCOSITY | STRENGTH | TEMP RANGE | CURE SPEED FIXTURE FULL | SPECIFIC GRAVITY | MILL SPECS A46050 C | |
|
General purpose instant adhesives ideal for rubber & plastic bonding. Versatile product line offering a complete range of viscosities & cure times.
|
RP
5 |
ETHYL |
CLEAR |
0.002 | 5 cps |
2700/4300 |
-65 to +200
F |
<5 Sec 8Hours | 1.05 |
Type II, Class
1 |
|
RP
5L |
ETHYL |
CLEAR |
0.005 | 5 cps |
2700/4300 |
-65 to +200
F |
<10 Sec 8Hours | 1.05 |
Type II, Class
1 | |
|
RP
30 |
ETHYL |
CLEAR |
0.003 | 30 cps |
2700/4300 |
-65 to +200
F |
<10 Sec 8Hours | 1.05 |
Type II, Class
1 | |
|
RP
45 |
ETHYL |
CLEAR |
0.004 | 45 cps |
2700/4300 |
-65 to +200
F |
<8 Sec 8Hours | 1.05 |
Type II, Class
1 | |
|
RP
100 |
ETHYL |
CLEAR |
0.006 | 100 cps |
2700/4300 |
-65 to +200
F |
<10 Sec 8Hours | 1.05 |
Type II, Class
2 | |
|
RP
200 |
ETHYL |
CLEAR |
0.005 | 200 cps |
2700/4300 |
-65 to +200
F |
<10 Sec 8Hours | 1.05 |
Type II, Class
2 | |
|
RP
500 |
ETHYL |
CLEAR |
0.007 | 500 cps |
2700/4300 |
-65 to +200
F |
<10 Sec 8Hours | 1.05 |
Type II, Class
2 | |
|
RP
750 |
ETHYL |
CLEAR |
0.007 | 750 cps |
2700/4300 |
-65 to +200
F |
<12 Sec 8Hours | 1.05 |
Type II, Class
2 | |
|
RP
1000 |
ETHYL |
CLEAR |
0.008 | 1,000 cps |
2700/4300 |
-65 to +200
F |
<15 Sec 8Hours | 1.09 |
Type II, Class
3 | |
|
RP
1500 |
ETHYL |
CLEAR |
0.008 | 1,500 cps |
2700/4300 |
-65 to +200
F |
<15 Sec 8Hours | 1.09 |
Type II, Class
3 | |
|
RP
2000 |
ETHYL |
CLEAR |
0.008 | 2,000 cps |
2700/4300 |
-65 to +200
F |
<15 Sec 8Hours | 1.09 |
Type II, Class
3 | |
|
RP
2400 |
ETHYL |
CLEAR |
0.008 | 2,400 cps |
2700/4300 |
-65 to +200
F |
<15 Sec 8Hours | 1.09 |
Type II, Class
3 | |
|
RP 3200
|
ETHYL |
CLEAR |
0.008 | 3,200 cps |
2700/4300 |
-65 to +200
F |
<15 Sec 8Hours | 1.09 |
Type II, Class
3 | |
|
RP
4000 |
ETHYL |
CLEAR |
0.008 | 4,000 cps |
2700/4300 |
-65 to +200
F |
<15 Sec 8Hours | 1.09 |
Type II, Class
3 | |
|
APS GEL |
ETHYL |
CLEAR |
0.010 | Gel |
2700/4300 |
-65 to +200
F |
<25 Sec 8Hours | 1.05 |
Type II, Class
3 |
| M SERIES, METAL BONDING SERIES |
| PRODUCT |
BASE |
COLOR | GAP FILL | VISCOSITY | STRENGTH | TEMP RANGE | CURE SPEED FIXTURE FULL | SPECIFIC GRAVITY | MILL SPECS A46050 C | |
|
Metal bonding instant adhesives used to bond metal to itself and other substrates. Available in a complete range of products. |
M 5 |
METHYL |
CLEAR |
.002 | 5 cps |
2800/4000 |
-85 to +200
F |
<5 Sec 8Hours | 1.07 |
Type 1, Class
1 |
|
M 60 |
METHYL |
CLEAR |
.004 | 60 cps |
2800/4000 |
-85 to +200
F |
<8 Sec 8Hours | 1.07 |
Type 1, Class
2 | |
|
M 100 |
METHYL |
CLEAR |
.006 | 100 cps |
2800/4000 |
-85 to +200
F |
<10 Sec 8Hours | 1.09 |
Type 1, Class
2 | |
|
M 1000 |
METHYL |
CLEAR |
.008 | 1,000 cps |
2800/4000 |
-85 to +200
F |
<10 Sec 8Hours | 1.09 |
Type II, Class
2 |
|
SI SERIES, SURFACE INSENSITIVE CYANOACRYLATE ADHESIVES |
| PRODUCT |
BASE |
COLOR | GAP FILL | VISCOSITY | STRENGTH | TEMP RANGE | CURE SPEED FIXTURE FULL | SPECIFIC GRAVITY | MILL SPECS A46050 C | |
|
Surface insensitive instance adhesives used in applications that require exceptionally fast cure speeds, on difficult to bond surfaces, and acidic surfaces, wood, PVC, substrates that contain plasticizers, certain types of EPDM, etc. Excellent for all surfaces.
|
SI 5 |
ETHYL |
CLEAR |
.002 | 5 cps |
2800/4200 |
-65 to +200
F |
<5 Sec 8Hours | 1.05 |
Type ll, Class
1 |
|
SI 30 |
ETHYL |
CLEAR |
.004 | 30 cps |
2800/4200 |
-65 to +200
F |
<5 Sec 8Hours | 1.05 |
Type ll, Class
1 | |
|
SI 120 |
ETHYL |
CLEAR |
.006 | 100 cps |
2800/4200 |
-65 to +200
F |
<8 Sec 8Hours | 1.05 |
Type ll, Class
2 | |
|
SI 500 |
ETHYL |
CLEAR |
.007 | 500 cps |
2800/4200 |
-65 to +200
F |
<8 Sec 8Hours | 1.05 |
Type II, Class
2 | |
|
SI 1000 |
ETHYL | CLEAR | .008 | 1000 cps | 2800/4200 | -65 to +200 F | <8 Sec 8Hours | 1.5 | Type II, Class 3 | |
|
SI 1500 |
ETHYL | CLEAR | .008 | 1500 cps | 2800/4200 | -65 to +200 F | <8 Sec 8Hours | 1.05 | Type II, Class 3 | |
|
SI 2000 |
ETHYL | CLEAR | .009 | 2000 cps | 2800/4200 | -65 to +200 F | <8 Sec 8Hours | 1.07 | Type II, Class 3 | |
| SI 3200 | ETHYL | CLEAR | .009 | 3200 cps | 2800/4200 | -65 to +200 F | <10 Sec 4Hours | 1.09 | Type II, Class 3 | |
| SI 4000 | ETHYL | CLEAR | .009 | 4000 cps | 2800/4200 | -65 to +200 F | <10 Sec 8Hours | 1.09 | Type II, Class 3 | |
| SI GEL | ETHYL | CLEAR | .010 | GEL | 2800/4200 | -65 to +200 F | <10 Sec 8Hours | 1.05 | Type II, Class 3 |
|
FS SERIES, FAST SETTING CYANOACRYLATE ADHESIVES |
| PRODUCT |
BASE |
COLOR | GAP FILL | VISCOSITY | STRENGTH | TEMP RANGE | CURE SPEED FIXTURE FULL | SPECIFIC GRAVITY | MILL SPECS A46050 C | |
|
Fast curing instant adhesives. The latest technology in cyanoacrylates, ideal in applications where low moisture conditions exist and/or exceptionally fast fixture times are desired. Bonds to a wide range of materials. |
FS 5 |
MODIFIED/ETHYL |
CLEAR |
.002 | 5 cps |
2700/4200 |
-65 to +200
F |
<2.5 Sec 4Hours | 1.05 |
Type ll, Class
1 |
|
FS 30 |
MODIFIED/ETHYL |
CLEAR |
.003 | 30 cps |
2700/4200 |
-65 to +200
F |
<2.5 Sec 4Hours | 1.05 |
Type ll, Class
1 | |
|
FS 100 |
MODIFIED/ETHYL |
CLEAR |
.006 | 100 cps |
2700/4200 |
-65 to +200
F |
<5 Sec 4Hours | 1.05 |
Type ll, Class
2 | |
|
FS 500 |
MODIFIED/ETHYL |
CLEAR |
.007 | 500 cps |
2700/4200 |
-65 to +200
F |
<5 Sec 4Hours | 1.05 |
Type II, Class
2 | |
|
FS1000 |
MODIFIED/ETHYL | CLEAR | .008 | 1000 cps | 2700/4200 | -65 to +200 F | <7.5 Sec 4Hours | 1.09 | Type II, Class 3 | |
|
FS 1500 |
MODIFIED/ETHYL | CLEAR | .008 | 1500 cps | 2700/4200 | -65 to +200 F | <7.5 Sec 4Hours | 1.09 | Type II, Class 3 | |
|
FS 2000 |
MODIFIED/ETHYL | CLEAR | .008 | 2000 cps | 2700/4200 | -65 to +200 F | <7.5 Sec 4Hours | 1.09 | Type II, Class 3 | |
| FS 3200 | MODIFIED/ETHYL | CLEAR | .008 | 3200 cps | 2700/4200 | -65 to +200 F | <7.5 Sec 4Hours | 1.09 | Type II, Class 3 | |
| FS 4000 | MODIFIED/ETHYL | CLEAR | .008 | 4000 cps | 2700/4200 | -65 to +200 F | <7.5 Sec 8Hours | 1.09 | Type II, Class 3 | |
| FS GEL | MODIFIED/ETHYL | CLEAR | .010 | GEL | 2700/4200 | -65 to +200 F | <12.5 Sec 4Hours | 1.05 | Type II, Class 3 |
| TS SERIES, CLEAR, TOUGHENED INSTANT ADHESIVE |
| PRODUCT |
BASE |
COLOR | GAP FILL | VISCOSITY | STRENGTH | TEMP RANGE | CURE SPEED FIXTURE FULL | SPECIFIC GRAVITY | MILL SPECS A46050 C | |
|
Excellent impact resistance and thermocycling properties. Ideal for bonding dissimilar materials on a wide range of surfaces.
|
TS 300 |
MODIFIED/ETHYL |
CLEAR |
.006 | 300 cps |
3750 |
-85 to +200
F |
<10 Sec 8Hours | 1.10 |
Type ll, Class
2 |
|
TS 800 |
MODIFIED/ETHYL |
CLEAR |
.008 | 800 cps |
3750 |
-85 to +200
F |
<15 Sec 8Hours | 1.10 |
Type ll, Class
3 | |
|
TS 2400 |
MODIFIED/ETHYL |
CLEAR |
.010 | 2400 cps |
3750 |
-85 to +200
F |
<15 Sec 8Hours | 1.10 |
Type ll, Class
3 | |
|
TS 5000 |
MODIFIED/ETHYL |
CLEAR |
.010 | 5,000cps |
37503750 |
-85 to +200
F |
<18 Sec 8Hours | 1.10 |
Type II, Class
3 |
| HP SERIES, BLACK, TOUGHENED INSTANT ADHESIVE |
| PRODUCT |
BASE |
COLOR | GAP FILL | VISCOSITY | STRENGTH | TEMP RANGE | CURE SPEED FIXTURE FULL | SPECIFIC GRAVITY | MILL SPECS A46050 C | |
|
Excellent peel, impact, shear strength and thermocycling properties. Ideal for bonding dissimilar materials on a wide range of surfaces. |
HP 300 |
MODIFIED/ETHYL |
BLACK |
.006 | 300 cps |
3750 |
-65 to +250
F |
<10 Sec 8Hours | 1.10 |
Type ll, Class
2 |
|
HP 1000 |
MODIFIED/ETHYL |
BLACK |
.009 | 1000 cps |
3750 |
-65 to +250
F |
<12 Sec 8Hours | 1.10 |
Type ll, Class
3 | |
|
HP 4000 |
MODIFIED/ETHYL |
BLACK |
.010 | 4000 cps |
3750 |
-65 to +250
F |
<18 Sec 8Hours | 1.10 |
Type ll, Class
3 | |
|
HP
10,000 |
MODIFIED/ETHYL |
BLACK |
.012 | 10,000 cps |
3500 |
-65 to +250
F |
<20 Sec 8Hours | 1.10 |
|
| NI SERIES, LOW ODOR/LOW BLOOM INSTANT ADHESIVE (Butyl) |
| PRODUCT |
BASE |
COLOR | GAP FILL | VISCOSITY | STRENGTH | TEMP RANGE | CURE SPEED FIXTURE FULL | SPECIFIC GRAVITY | |
|
low odor/low bloom instant adhesives. Greatly reduces frosting on parts and the need for sophisticated ventilation.
|
NI 5 |
BUTYL |
CLEAR |
.002 | 5 cps |
1900/3000 |
-65 to +180
F |
<7 Sec 24Hours | 1.05 |
|
NI 100 |
BUTYL |
CLEAR |
.005 | 100 cps |
1900/3000 |
-65 to +180
F |
<7 Sec 24Hours | 1.05 | |
|
NI 500 |
BUTYL |
CLEAR |
.007 | 500 cps |
1900/2900 |
-65 to +180
F |
<20 Sec 24Hours | 1.05 | |
|
NI 1000 |
BUTYL |
CLEAR |
.008 | 1,000 cps |
1900/3000 |
-65 to +180
F |
<7 Sec 24Hours | 1.05 |
| NI "E" SERIES, LOW ODOR/LOW BLOOM INSTANT ADHESIVE (Butyl) |
| PRODUCT |
BASE |
COLOR | GAP FILL | VISCOSITY | STRENGTH | TEMP RANGE | CURE SPEED FIXTURE FULL | SPECIFIC GRAVITY | |
|
low odor/low bloom instant adhesives. Eliminates frosting and odors typically associated with cyanoacrylates.
|
NI 5E |
MODIFIED |
CLEAR |
.002 | 5 cps |
1900/2700 |
-65 to +180
F |
<10 Sec 24Hours | 1.10 |
|
NI 100E |
MODIFIED |
CLEAR |
.006 | 100 cps |
1900/2700 |
-65 to +180
F |
<10Sec 24Hours | 1.10 | |
|
NI 500E |
MODIFIED |
CLEAR |
.007 | 500 cps |
1900/2700 |
-65 to +180
F |
<25 Sec 24Hours | 1.10 | |
|
NI 1000E |
MODIFIED |
CLEAR |
.008 | 1,000 cps |
1900/2700 |
-65 to +180
F |
<10Sec 24Hours | 1.10 |
|
HT SERIES, HIGH TEMPERATURE CYANOACRYLATE ADHESIVES |
| PRODUCT |
BASE |
COLOR | GAP FILL | VISCOSITY | STRENGTH | TEMP RANGE | CURE SPEED FIXTURE FULL | SPECIFIC GRAVITY | MILL SPECS A46050 C | |
|
Excellent high end temperature resistance. Ideal for applications that have a high degree of temperature cycling and/or extended operation at elevated temperature. |
HT 5 |
MODIFIED/ETHYL |
CLEAR |
.002 | 5 cps |
2700/4200 |
-60 to +275
F |
<7 Sec 8Hours | 1.06 |
Type ll, Class
1 |
|
HT 30 |
MODIFIED/ETHYL |
CLEAR |
.003 | 30 cps |
2700/4200 |
-60 to +275 F | <12 Sec 8Hours | 1.06 |
Type ll, Class
1 | |
|
HT 100 |
MODIFIED/ETHYL |
CLEAR |
.006 | 100 cps |
2700/4200 |
-60 to +275 F | <14 Sec 8Hours | 1.06 |
Type ll, Class
2 | |
|
HT 500 |
MODIFIED/ETHYL |
CLEAR |
.007 | 500 cps |
2700/4200 |
-60 to +275 F | <14 Sec 8Hours | 1.6 |
Type II, Class
2 | |
|
HT 1000 |
MODIFIED/ETHYL | CLEAR | .008 | 1000 cps | 2700/4200 | -60 to +275 F | <18 Sec 8Hours | 1.09 | Type II, Class 3 | |
|
HT 1500 |
MODIFIED/ETHYL | CLEAR | .008 | 1500 cps | 2700/4200 | -60 to +275 F | <18 Sec 8Hours | 1.09 | Type II, Class 3 | |
|
HT 2400 |
MODIFIED/ETHYL | CLEAR | .008 | 2400cps | 2700/4200 | -60 to +275 F | <18 Sec 8Hours | 1.09 | Type II, Class 3 | |
| HT 4000 | MODIFIED/ETHYL | CLEAR | .008 | 4000 cps | 2700/4200 | -60 to +275 F | <20Sec 8Hours | 1.09 | Type II, Class 3 |
|
MG SERIES, MEDICAL GRADE INSTANT ADHESIVES (USP CLASS VI) |
| PRODUCT |
BASE |
COLOR | GAP FILL | VISCOSITY | STRENGTH | TEMP RANGE | CURE SPEED FIXTURE FULL | SPECIFIC GRAVITY | MILL SPECS A46050 C | |
|
Medical grade instant adhesives. These products have USP Class Vl Certification and are used in assembling medical devices.
|
MG
5 |
ETHYL |
CLEAR |
.002 | 5 cps |
2700/4300 |
-65 to +200
F |
<15 Sec 8Hours | 1.05 |
Type ll, Class
1 |
|
MG 30 |
ETHYL |
CLEAR |
.003 | 30 cps |
2700/4300 |
-65 to +200
F |
<15 Sec 8Hours | 1.05 |
Type ll, Class
1 | |
|
MG 100 |
ETHYL |
CLEAR |
.006 | 100 cps |
2700/4300 |
-65 to +200
F |
<15 Sec 8Hours | 1.05 |
Type ll, Class
2 | |
|
MG 500 |
ETHYL |
CLEAR |
.007 | 500 cps |
2700/4300 |
-65 to +200
F |
<15 Sec 8Hours | 1.05 |
Type II, Class
2 | |
|
MG 1000 |
ETHYL | CLEAR | .008 | 1000 cps | 2700/4300 | -65 to +200 F | <15 Sec 8Hours | 1.09 | Type II, Class 3 | |
|
MG 1500 |
ETHYL | CLEAR | .008 | 1500 cps | 2700/4300 | -65 to +200 F | <15 Sec 8Hours | 1.09 | Type II, Class 3 | |
|
MG 2400 |
ETHYL | CLEAR | .008 | 2400 cps | 2700/4300 | -65 to +200 F | <15 Sec 8Hours | 1.09 | Type II, Class 3 | |
| MG 3200 | ETHYL | CLEAR | .008 | 3200 cps | 2700/4300 | -65 to +200 F | <15 Sec 8Hours | 1.09 | Type II, Class 3 | |
| MG 4000 | ETHYL | CLEAR | .008 | 4000 cps | 2700/4300 | -65 to +200 F | <15 Sec 8Hours | 1.09 | Type II, Class 3 |